ANALISIS UJI TARIK KOMPOSIT SERAT BATANG KELAKAI DENGAN VARIASI KATALIS UNTUK PEMBUATAN MATERIAL BUMPER MOBIL
DOI:
https://doi.org/10.22437/jop.v9i1.27670Keywords:
Komposit; Kelakai; Katalis; Kekuatan Tarik; BumperAbstract
A research was conducted to create car bumper materials using natural kelakai plant fibers combined with a catalyst and resin as a binding agent in the composite. The main goal of the study was to examine the tensile strength of the kelakai fiber composite with different catalyst variations and assess the impact of these catalyst changes on the bumper material's tensile strength. The composite materials were prepared in three test specimens with catalyst compositions of 2,5%, 5%, and 7,5%, respectively, based on a 20 mL resin composition. These samples underwent tensile testing using a Universal Testing Machine (UTM). The results revealed that the tensile strength of the kelakai fiber composite increased with higher catalyst percentages. At 2,5%, 5%, and 7,5% catalyst compositions, the tensile strengths were measured as 0,37 N/mm2, 0,41 N/mm2, and 0,47 N/mm2, respectively. Additionally, the elongation values for the catalyst portion are 1,11%, 2,22%, and 3,89% and the Young's modulus values are 0,33 N/mm2, 0,18 N/mm2, and 0,12 N/mm2, respectively. The study demonstrates the significant influence of catalyst variations on the tensile strength of the kelakai fiber composite.
Downloads
References
Agustin, R. D. 2014. Kekuatan Tarik dan Modulus Elastisitas Bahan Komposit Berpenguat Serat Ampas Tebu dan Matrik Asam Polilaktat. Tugas Akhir. Jurusan Fisika Program Sarjana Universitas Jember (Dipublikasikan).
Alamsyah, T. Hidayat, dan A. N. Iskandar. 2021. Pengaruh Perbandingan Resin dan Katalis terhadap Kekuatan Tarik Komposit Fiberglass-Polyester untuk Bahan Pembuatan Kapal. Zona Laut: Jurnal Inovasi Sains dan Teknologi Kelautan, 2(2): 26-32.
Ezekwem, C. I. W. 2016. Composite Materials Literature Review for Car Bumper. Journal ResearchGate. Department of Physics Loughborough University.
Hanifi, R., G. B. Dewangga, Kardiman, dan E. Widianto. 2019. Analisis Material Komposit Berbasis Serat Pelepah Kelapa Sawit dan Matriks Polypropylene sebagai Bahan Pembuatan Bumper Mobil. Gorontalo Journal of Infrastructure and Science Engineering, 2(2): 15-23.
Hestiawan, H., Jamasri, dan Kusmono. 2017. Pengaruh Penambahan Katalis terhadap Sifat Mekanis Resin Poliester Tak Jenuh. Jurnal Teknosia, 3(1): 1-7.
Lokantara, I. P., N. P. G. Suardana, I. M. G. Karohika, dan Nanda. 2010. Pengaruh Panjang Serat pada Temperatur Uji yang Berbeda terhadap Kekuatan Tarik Komposit Polyester Serat Tapis Kelapa. Jurnal Ilmiah Teknik Mesin CakraM, 4(2): 166-172.
Maryanti, B., A. A. Sonief, dan S. Wahyudi. 2011. Pengaruh Alkalisasi Komposit Serat Kelapa-Poliester terhadap Kekuatan Tarik. Jurnal Rekayasa Mesin, 2(2): 123-129.
Milya, R., S. Syahril, A. Yufrizal dan R. A. Nabawi. 2022. Pengaruh Persentase Resin dan Katalis terhadap Kekuatan Tarik Komposit Fiberglass. Jurnal Vokasi Mekanika, 4(3): 78-83.
Perwara, A. S. 2021. Pengaruh Persentase Katalis terhadap Sifat Mekanis Komposit Bermatrik Resin Polyester. Approach: Jurnal Teknologi Penerbangan, 5(2): 6-13.
Poul, K., M. S. Y. Lubis, dan S. Ariyanti. 2022. Analis Numerik Sifat Mekanik Bahan ABS & Komposit Serat Bambu Aplikasi Pada Komponen Adjuster Seat Mobil. Jurnal Penelitian dan Aplikasi Sistem dan Teknik Industri (PASTI), 16(1): 14-26.
Pratama, Y. Y., R. H. Setyanto, dan I. Priadythama. 2014. Pengaruh Perlakuan Alkali, Fraksi Volume Serat dan Panjang Serat terhadap Kekuatan Tarik Komposit Serat Sabut Kelapa-Polyester. Jurnal Ilmiah Teknik Industri, 13(1): 8-15.
Rintami, M. 2022. Pengaruh Campuran Serat Alam Komposit Kulit Kayu Akasia dan Tandan Kosong Kelapa Sawit Menggunakan Perangkat Resin Epoxy terhadap Sifat Mekanis. Tugas Akhir. Jurusan Teknik Mesin Program Sarjana Universitas Islam Riau (Dipublikasikan).
Saidah, A., S. E. Susilowati, dan Y. Nofendri. 2018. Analisa Perbandingan Kekuatan Tarik dan Impak Komposit Serat Jerami Padi Polyester dengan Komposit Serat Jerami Padi-Epoxy dengan Metode Hand Lay Up. Prosiding SNAST, 291-298.
Saidah, A., S. E. Susilowati, dan Y. Nofendri. 2018. Pengaruh Fraksi Volume dan Orientasi Serat terhadap Kekuatan Tarik Komposit Berbahan Serat Rami Epoxy sebagai Bahan Alternatif Komponen Otomotif. Seminar Nasional Teknik Mesin, 191-197.
Verma, D., dan I. Senal. 2019. Natural Fiber-Reinforced Polymer Composites: Feasibility Study for Sustainable Automotive Industries. Thailand : Woodhead Publishing Series in Composites Science and Engineering, 103-122.
Widiarta, I. W., N. P. Nugraha, dan K. R. Dantes. 2018. Pengaruh Orientasi Serat terhadap Sifat Mekanik Komposit Berpenguat Serat Alam Batang Kulit Waru (Hibiscus tiliaceust) dengan matrik Polyester. Jurnal Pendidikan Teknik Mesin Undiksha, 6(1): 41-57.